Elektroda Karbon Dari Biomassa Kulit Buah Mahoni Dengan Penambahan Tiourea Untuk Aplikasi Sel Superkapasitor

---

ABSTRACT
Biomass is a renewable energy source that can be converted into carbon material for supercapacitor energy storage devices. This study used mahogany rind biomass as carbon electrodes for supercapacitor cells without the addition of thiourea and with the addition of 0,5 and 1g thiourea. The process of fabrication carbon electrodes begins with a pre-carbonization process with a temperature of 200˚C, after that, a chemical activation process was carried out using KOH with a concentration of 0,1 M, then the carbonization process with N2 gas at a temperature of 600˚C and followed by physical activation with CO2 gas at a temperature 800˚C. The highest density shrinkage value is owned by the KBM-0 sample, which is 45,04%. Fourier Transform Infra Red analysis shows that the activated carbon of mahogany rind contains functional groups O-H, C-H, S-H, C-C, C=O and C-O. X-Ray Diffraction analysis shows that there are two broad peaks at an angle of 2θ 22˚-24˚ and 43˚ in the scattering plane (002) and (100) which identify amorphous characteristics. Scanning Electron Microscopy analysis shows the formation of porous carbon electrodes with mesoporous and nanofiber morphological structures. Energy Dispersive X-Ray analysis show that the KBM-0 sample has the highest carbon content, at 96,19%. The results of electrochemical analysis of supercapacitor cells using the Cyclic Voltametry and Galvanostatic Charge-Discharge methods with 1 M H2SO4 electrolyte, yielded the highest specific capacitance values owned by the KBM-0 sample of 375,47 Fg-1 and 384,67 A/g, respectively. In conclusion, the biomass of mahogany rind can be used as a porous carbon electrode for the application of high-performance supercapacitor cells.
Keywords: Biomass, Mahogany Fruit Peel, Supercapacitor

---

Ketersediaan

Informasi Detail

Judul Seri

-

No. Panggil

1903110094

Penerbit

Pekanbaru : Universitas Riau - FMIPA - Fisika., 2023

Deskripsi Fisik

-

Bahasa

Indonesia

ISBN/ISSN

-

Klasifikasi

1903110094

Tipe Isi

-

Tipe Media

-

Tipe Pembawa

-

Edisi

-

Subjek

FISIKA

Info Detail Spesifik

-

Pernyataan Tanggungjawab

TIAR

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus masuk sebelum memberikan komentar