Pengaruh Suhu Dan Persen Katalis Zeolit Terhadap Yield Pirolisis Limbah Plastik Polypropylene (Pp)

---

Increasing population growth leads to increased plastic waste resulting in adverse environmental impacts, If not further processed. This research was conducted to convert plastic waste into fuel oil using synthetic zeolite catalyst. The purpose of this research is to see the influence of temperature variation and percent catalyst / plastic. A total of 100 grams of polypropylene plastic type were crushed in a batch reactor at a temperature of 300 ° C, 350 ° C, and 400 ° C for 60 minutes with percent catalyst / plastic variations 5; 6; 7 (% weight). The highest yield was obtained at 400 ° C with 7% catalyst / plastic percent of 75.69%. While the highest yield without catalyst was obtained at 400 ° C at 65.57%. The product result obtained is density 0,87 gr / ml, kinematic viscosity value 2,140 cSt, flash point value 52 °C, calorific value 44.673 kJ / kg. The analysis results show that (%) yield of the product meets the diesel (solar) standard. Keywords: liquid fuel, heating value, pyrolysis, polypropylene, synthetic zeolite.

---

Ketersediaan

Informasi Detail

Judul Seri

-

No. Panggil

07 02. 117 (0052)

Penerbit

Pekanbaru : Universitas Riau – Fakultas Teknik – Lingkungan., 2017

Deskripsi Fisik

xv, 69 hlm.: ill.; 29 cm

Bahasa

Indonesia

ISBN/ISSN

-

Klasifikasi

07 02. 117 (0052)

Tipe Isi

-

Tipe Media

-

Tipe Pembawa

-

Edisi

-

Subjek

LINGKUNGAN

Info Detail Spesifik

-

Pernyataan Tanggungjawab

DAUS

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus masuk sebelum memberikan komentar