Sifat Dan Morfologi Wood Plastic Composite Berbasis Pelepah Sawit/Polietilen Dengan Kompatibiliser Maleic Anhidryde Dan Inisiator Benzoil Peroksida

---

The low compatibility between thermoplastic and wood components is a major problem in the manufacture of wood plastic composite. Compatibilities used such as maleic anhydride is useful to increase the value of the mechanical and physical properties of the WPC. The purpose of this study is to determine the effect of the composition palm frond/polyethylene and maleic anhydride on the properties and morphology of wood plastic composite. The composition of palm frond/polyethylene used is 50/50, 60/40, 70/30 with a mixture of 2% paraffin additive, maleic anhydride (MAH) 3%, 4%, 5%, and benzoyl peroxide 1% of the weight of MAH. The process of mixing fillers, matrices, and additives uses an Internal Mixer Labo Plastomill at temperature of 145oC and rotor speed of 80 rpm. The sample was then pressed using a hot press at a temperature of 145oC and a pressure of 100 kgf/cm2. Composites produced were tested including characterization of functional groups, morphological conditions, physical properties and mechanical properties. The results showed that the addition of filler and maleic anhydride composition had a relatively significant effect. The best WPC material is found in the variation palm frond/polyethylene 60/40 and MAH 5% with a density value of 1.19 gr/cm3, water content of 0.16%, water absorption capacity of 0.41%, swelling thickness of 0.11%, tensile strength of 18.664 MPa, elastic modulus of 2175.9 MPa, and flexural strength of 35.05 MPa.
Keywords:

---

Ketersediaan

Informasi Detail

Judul Seri

-

No. Panggil

07 02. 118 (0119)

Penerbit

Pekanbaru : Universitas Riau – Fakultas Teknik – Teknik Kimia., 2018

Deskripsi Fisik

xi, 71 hlm.; ill.; 29 cm

Bahasa

Indonesia

ISBN/ISSN

-

Klasifikasi

07 02. 118 (0119)

Tipe Isi

-

Tipe Media

-

Tipe Pembawa

-

Edisi

-

Subjek

KIMIA

Info Detail Spesifik

-

Pernyataan Tanggungjawab

DAUS

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus masuk sebelum memberikan komentar