Kualitas Papan Partikel Dari Limbah Serabut Kelapa Sawit Dengan Perekat Damar

---

ABSTRACT
Palm fiber is a waste of crude palm oil processing that has not been used
optimally. This study aims to obtain the best resin adhesive concentration in the
manufacture of particle board from palm oil fibers. The research was conducted
experimentally using a completely randomized design (CRD) with 5 treatments
and 3 replications. The treatment in this study was the ratio of oil palm fiber and
resin adhesive as follows: P1 (90 : 10), P2 (88 : 12), P3 (86 : 14), P4 (84 : 16), P5
(82 : 18). The data obtained were analyzed statistically using Analysis of Variance
(ANOVA) and Duncan New Multiple Range Test (DNMRT) at the 5% level. The
results showed that the composition of oil palm fiber and resin adhesive had a
significant effect on density, water absorption, thickness expansion, modulus of
elasticity, and modulus of rapture but had no significant effect on moisture
content. The best treatment chosen was treatment P5 with a density value of 0.93
g/cm3, 4.49% water content, 54% water absorption, 37% thickness development,
1283.47 kgf/cm2 modulus of elasticity, 13.03 kgf/cm2 modulus of rupture.
Keywords : Particle board, palm fiber, resin adhesive

---

Ketersediaan

Informasi Detail

Judul Seri

-

No. Panggil

06 03. 121 (0020)

Penerbit

Pekanbaru : Universitas Riau – Fakultas Pertanian - Teknologi Pertanian., 2021

Deskripsi Fisik

ix, 77 hlm.; ill.: 29 cm

Bahasa

Indonesia

ISBN/ISSN

-

Klasifikasi

06 03. 121 (0020)

Tipe Isi

-

Tipe Media

-

Tipe Pembawa

-

Edisi

-

Subjek

TEKNOLOGI PERTANIAN

Info Detail Spesifik

-

Pernyataan Tanggungjawab

Daus

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus masuk sebelum memberikan komentar