Studi Kinetika Reaksi Pada Proses Deasetilasi Kitin Dari Limbah Industri Ebi

---

Chitosan is used in a variety of industrial applications, such as purification agents, flocculation agents, anti-microbial agents, biological adhesives, anti-tumor agents and the cosmetic industry. This study studied deacetylation reaction kinetics and the effect of particle size difference on chitosan formation of chitin using raw materials of ebi industry waste. Chitosan was obtained by deproteination, demineralization and deacetylation using 50% NaOH with a ratio of 1:20 (w / v) at a temperature of 80 ° C. Samples were analyzed using FTIR sprestroscopy and acid-base titration. The results showed deacetylation degree at minute 120 for chitin diameter 0.25, 0.177, 0.152 mm were 51.51, 64.39, and 78.87%, respectively. The reaction mechanism is determined by model matching using the SSE value of the model against the value of the data obtained. The result show that model is not appropriate, but among the three models tested, the 2nd model is the closest model. This corresponds to the value of the obtained diffusivity for each sample ranging from 0.25, 0.177 and 0.152 mm diameters respectively of 1.841. 10-18, 2.657. 10-18, and 3.085 .10-18 m2/s.
Keywords : Deacetylation, reaction kinetics, chitosan, ebi’s waste, shrinking unreacted core model

---

Ketersediaan

Informasi Detail

Judul Seri

-

No. Panggil

07 02. 118 (0048)

Penerbit

Pekanbaru : Universitas Riau – Fakultas Teknik – Teknik Kimia., 2018

Deskripsi Fisik

xiii, 77 hlm.; ill.; 29 cm

Bahasa

Indonesia

ISBN/ISSN

-

Klasifikasi

07 02. 118 (0048)

Tipe Isi

-

Tipe Media

-

Tipe Pembawa

-

Edisi

-

Subjek

KIMIA

Info Detail Spesifik

-

Pernyataan Tanggungjawab

DAUS

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus masuk sebelum memberikan komentar