Karakteristik Mekanik Komposit Polymeric Foam Dengan Matriks Polyester Resin Serat Tandan Kosong Sawit (Tks), Serat Pinang, Dan Kombinasi Serat Tks-Pinang

---

In this era, research are application of composite such as furniture, aerospace, automotive components fabricated by synthetic fibers. Natural fibers can substitute of synthetic fibers. The one of natural fiber OPEFB is composite was waste residue of the processing palm oil utilization which use as compost and fuel of combustion proces in boiler palm oil mill. Generally, the part of areca usually use is nut, while fibers are throw 5% NaOH for 4 hours and boiling distilled water for 1 hour as a composite of a polymeric foam to the mechanical properties of the composite. OPEFB and areca fibers use as the reinforcement and polyester resin use as matrix. In this research, method of manufacture used Vacuum Assisted Resin Infusion (VARI). The results showed the highest value of yield strength is 4.76 MPa, tensile strength is 16.08 MPa, fracture strength is 16.08 MPa in the areca fiber composite treatment NaOH 5%, for elastic modulus is 22.49 MPa in the areca fiber treatment of boiling distilled water, total engineering strain 7.81% in the OPEFB fiber composite where soaking treatment of 5% NaOH. Impact strength of 1.38 J/mm2 in the OPEFB fiber composite treatment immersion of 5% NaOH.
Keywords : areca fiber, boiling distilled water, NaOH 5%, OPEFB, polyester resin, VARI.

---

Ketersediaan

Informasi Detail

Judul Seri

-

No. Panggil

07 03. 120 (0020)

Penerbit

Pekanbaru : Universitas Riau – Fakultas Teknik – Teknik Mesin., 2020

Deskripsi Fisik

xiv, 71 hlm.; ill.; 29 cm

Bahasa

Indonesia

ISBN/ISSN

-

Klasifikasi

07 03. 120 (0020)

Tipe Isi

-

Tipe Media

-

Tipe Pembawa

-

Edisi

-

Subjek

MESIN

Info Detail Spesifik

-

Pernyataan Tanggungjawab

DAUS

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus masuk sebelum memberikan komentar