CD Skripsi

Sintesis Partikel Komposit Magnetit/Hidroksiapatit Menggunakan Metode Hidrotermal

---

Magnetite/hydroxyapatite composites can be applied in biomedical fields such as drug delivery, orthopedics, protein adsorption/release, hyperthermia therapy, and solid phase extraction from plasmid DNA. The purpose of this study was to study the effect of reaction temperature and hydroxyapatite ratio on the crystallinity, particle size, magnetism and morphology of the composites of magnetite/hydroxyapatite synthesized using the hydrothermal method. Composites were synthesized from 2 mmol of FeCl3, 4 mmol of citrate and 6 mmol of urea which were dissolved in 40 ml of distilled water and stirred at 300 ppm using a magnetic stirrer for 15 minutes, then added 7.5 g/L polyethylene glycol and commercial hydroxyapatite of various concentrations (70%, 80% and 90%) and stirred again for 1 hour. Then the suspension was put into a hydrothermal container and in the oven at a temperature of 200oC, 220oC, and 240oC for 12 hours. The magnetite/hydroxyapatite composite particles obtained were then characterized by X-ray Diffraction (XRD), BET Brunauer-Emmett-Teller Analysis, Vibrating Sample Magnetometer (VSM), and Transmission Electron Mycroscope (TEM). The magnetite particles produced are cubicly shaped and hydroxyapatite were hexagonally shaped. The increase in reaction temperature from 200 oC to 240oC at the concentration of magnetite are 10% increased the crystals size of magnetite from 22,87 nm to 24,162 nm and crystal size of hydroxyapatite increased from 26,456 nm to 27,8 nm, decreased specific surface area from 27,434 m2/g to 18.083 m2/g, and decreased saturation magnetization (Ms) from 4,2 emu/g to 3,82 emu/g. While the increase in the concentration of magnetite in composite from 10% and 30% at 240oC increased the crystal size of magnetite from 24,162 nm to 27,472 nm, decreased the crystal size of hydroxyapatite from 27,8 nm to 26,288 nm, and increased specific surface area from 18,083 m2/g to 27,56 m2/g. Magnetite/hydroxyapatite composite were superparamagnetic with coercivity 0,2 Oe, The magnetites were spread evenly on the hydroxyapatite matrix with uniform particle shape and size, while the particle size of hydroxyapatite and magnetite was 25 nm and 17 nm respectively.Keywords: Composite, Magnetite, Hydroxyapatite, Hydrothermal, Drug Delivery System

---

Ketersediaan

Informasi Detail

Judul Seri

-

No. Panggil

07 02. 118 (0103)

Penerbit

Pekanbaru : Universitas Riau – Fakultas Teknik – Teknik Kimia., 2018

Deskripsi Fisik

xiv, 71 hlm.; ill.; 29 cm

Bahasa

Indonesia

ISBN/ISSN

-

Klasifikasi

07 02. 118 (0103)

Tipe Isi

-

Tipe Media

-

Tipe Pembawa

-

Edisi

-

Subjek

KIMIA

Info Detail Spesifik

-

Pernyataan Tanggungjawab

DAUS

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus masuk sebelum memberikan komentar