ABSTRACT
Palm frond is biomass that has not been widely used as a renewable energy
source. Torrefaction is a pretreatment process to improve the quality of the
biomass as solid fuel. The aims of this research was to made briquette from palm
frond which appropriate with SNI, and then to determined the effects of particle
size, pressure and filler composition on response toward calorific value and
pressure using Responce Surface Methodology (RSM). Palm frond uses sieve 60,
80 and 100 mesh. Pressure 100, 110 and 120 kg/cm2, and tapioca adhesive
composition 10, 20 and 30%-wt. The highest calorific value was 3989,05 cal/g
which obtained at 100 mesh of particle size, pressure 120 kg/cm2, and filler
compostion 10%-wt. The highest pressure was 8,92759 kg/cm2 which obtained at
100 mesh of particle size, pressure 120 kg/cm2 and filler composition 30%-wt.
Process conditions is very influence significantly on the calorific value and
compressive strength is the composition of the adhesive and the pressing pressure.
Keywords : Briquette, Torrefaction, Responce Surface Methodology, Calorific
Value, Renewable Energy

---

Ketersediaan

Informasi Detail

Judul Seri

-

No. Panggil

07 02. 120 (0127)

Penerbit

Pekanbaru : Universitas Riau – Fakultas Teknik – Teknik Kimia., 2020

Deskripsi Fisik

xii, 29 hlm.; ill.: 29 cm

Bahasa

Indonesia

ISBN/ISSN

-

Klasifikasi

07 02. 120 (0127)

Tipe Isi

-

Tipe Media

-

Tipe Pembawa

-

Edisi

-

Subjek

TEKNIK KIMIA

Info Detail Spesifik

-

Pernyataan Tanggungjawab

Daus

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus masuk sebelum memberikan komentar