Karakterisasi Plastik Biodegradable Dari Pati Onggok Singkong Dan Nata De Coco

---

ABSTRACT
Tapioca solid waste from the processing of tapioca still contains starch, which can be used as a raw material for making biodegradable plastic. The purpose of this study was to obtain the best formulation in the manufacture of biodegradable plastics from cassava starch and nata de coco. This research was carried out experimentally using a completely randomized design (CRD). The treatments in this research were the ratio of tapioca solid waste and nata de coco, which are ON1(95:5), ON2(90:10), ON3(85:15) and ON4(80:20) in 10 g biodegradable plastic formulations. The results showed that the tapioca solid waste and nata de coco had a significantly affected on thickness, water resistance, water vapor transmission, tensile strength, elongation, and. biodegradation time. The best treatment chosen was ON4 ratio of tapioca solid waste and nata de coco (80:20) having thickness of 0.15 mm, water resistance 80.56% s, water vapor transmission 9.14 (g/m2/hour), tensile strength of 4.16 MPa, elongation of 33.81%, and biodegradation for 6th days.
Keywords : Biodegradable plastic, nata de coco, tapioca solid waste

---

Ketersediaan

Informasi Detail

Judul Seri

-

No. Panggil

06 04. 121 (0044)

Penerbit

Pekanbaru : Universitas Riau –Fakultas Pertanian – Teknologi Pertanian., 2021

Deskripsi Fisik

ix,112 hlm.: ill.: 29 cm

Bahasa

Indonesia

ISBN/ISSN

-

Klasifikasi

06 04. 121 (0044)

Tipe Isi

-

Tipe Media

-

Tipe Pembawa

-

Edisi

-

Subjek

TEKNOLOGI PERTANIAN

Info Detail Spesifik

-

Pernyataan Tanggungjawab

Daus

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus masuk sebelum memberikan komentar