Pengaruh Komposisi Polyethylene Glycol (Peg) Dalam Sintesis Dan Karakteristik Membran Kitosan-Silika Untuk Proses Pengolahan Limbah Cair Hotel

---

The membrane is a selective and semipermeable layer that is between two phases, namely the feed phase and the permeate phase. Membrane synthesis using chitosan-silica with phase inversion method. The purpose of this research were to make membranes of chitosan-silica for hotel waste water treatment with 0,5, 2,5 and 5 gram poly ethylene glycol. This research produced porous membrane. The characterization membranes analysis were SEM analysis, tensile strength, flux and rejection. Tensile strength analysis showed that membrane with the highest tensile strenghth was 19,14 Mpa for membrane with 0,5 gram composition of poly ethylene glycol. Based on Flux and rejection results showed that membrane with 2,5 gram composition of poly ethylene glycol was the most effective performance with the flux 18,19 L/m2.h and rejection elimination of BOD was 50,76%, COD was 46,09% and TSS was 48,00%.


Keywords : flux, membrane, rejection, ultrafiltration

---

Ketersediaan

Informasi Detail

Judul Seri

-

No. Panggil

07 02. 119 (0169)

Penerbit

Pekanbaru : Universitas Riau – Fakultas Teknik – Teknik Kimia D III., 2019

Deskripsi Fisik

vi, 71 hlm.; ill.; 29 cm

Bahasa

Indonesia

ISBN/ISSN

-

Klasifikasi

07 02. 119 (0169)

Tipe Isi

-

Tipe Media

-

Tipe Pembawa

-

Edisi

-

Subjek

KIMIA

Info Detail Spesifik

-

Pernyataan Tanggungjawab

DAUS

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus masuk sebelum memberikan komentar